e No part of this standard may be reproduced without the prior permission of DIN Deutsches Institut für Normung e.V., Berlin. In case of doubt, the. Buy DIN POLYETHYLEN COATINGS OF STEEL PIPES AND FITTINGS – REQUIREMENTS AND TESTINGS from SAI Global. DIN () Polyethylene coatings on steel pipes and fittings – Requirements and testing. Be notified when this Standard is updated or amended – Add.

Author: Dizragore Bajas
Country: Belize
Language: English (Spanish)
Genre: Travel
Published (Last): 27 July 2008
Pages: 293
PDF File Size: 11.25 Mb
ePub File Size: 11.96 Mb
ISBN: 118-9-82844-157-2
Downloads: 69753
Price: Free* [*Free Regsitration Required]
Uploader: Dokinos

For extruded coatings a differentiation is made between sleeve extrusion and sheet extrusion. The same applies to the relevant extrusion line parameters.

Please first log in with a verified email before subscribing to alerts. Drill a 6 mm hole through the coating down to the steel substrate. The sample thickness shall be 1,8 mm to 2,5 mm and shall be uniform throughout. The peak occurring further along the curve characterises the uncured portion of the material.

Coating pipe is the pipe that is by the processing after the corrosion, which can effectively prevent or slow the steel pipe occurs in the course of transport and chemical or electrochemical reaction corrosion phenomena.

Generally it is with7 days if the goods are in stock. DIN 0 refers to polyethylene coating on steel pipes and fittings — Requirements and tests. Welded Alloy Steel Pipe. The thickness of single layers and the total coating thickness shall be determined.

Determination of gel time of thermosetting coating powders at a given temperature DIN EN ISOPreparation of steel substrates before application of paints and related products — Visual assessment of surface cleanliness — Part 1: High quality Passed the ISO Today, findings confirm that the testing of new materials exposed to wetting agents at high temperatures does not have any significance as regards ageing-related stress cracking behaviour. For each segment determine, to an accuracy of 0,5 mm, the maximum length of disbondment measured from the edge of the artificial defect to the edge of original adhered area For system testing, calculate the arithmetic mean of three samples, and express the maximum length of disbondment expressed as the cathodic disbondment in mm.

  KUSTOM STOMPA PDF

Marking shall be carried out using a suitable method such as stencil painting or printing, and shall be durable and legible.

This standard is not included in any packages. Adhesive made of modified co-polymer of high quality is melted with factory PE main coat. In each case three measurements shall be taken. B PSL1 hot rolled carbon steel seamless pipe.

DIN 30670 seamless coating pipe with Polyethylene coatings

Supplier Types Trade Assurance. Then, attach the additional weight to the indenter and, after 24 h, read the depth of indentation indicated on the penetrometer scale. Packing In bulk 7. Made In China din coating pipe. The section should not be taken from the weld area. In case of doubt, the German-language original shall be considered authoritative. During measurement the counter electrode shall be immersed in the test medium. The final evaluation shall be carried out after the ageing time specified above for each type of coating.

If necessary, the bottom side of the test piece can be ground down to the desired thickness. Production control is assured by the coater. Contact Us Sales Team Network. J per mm of coating thickness. A noticeable air gap will distort the result.

DIN coated steel pipe with Polyethylene coatings

The test of the degree of cure of the epoxy resin coating by means of DSC measurement dinn also new, as is the cathodic disbondment test, which is frequently required at international level. Then, make another cut perpendicular to the axis of the previous cut to isolate the strip and lift 3670 length of about 20 mm from the pipe. Home About Us We are trusted. The total mass shall be 2,5 kg. After application the repair shall be verified in accordance with Annex E.

The instrument shall be suitable for and calibrated for the coating thickness range to be measured. Set the zero value within 5 s. There vin two kinds of procession by winding-wrap and full-coated. The present standard specifies requirements for coatings that are applied to longitudinally or spirally welded or seamless steel pipes and fittings used for the construction of pipelines for conveying liquids or gases.

  HIOKI 3196 PDF

You can ensure product safety by selecting from certified suppliers, including 31 with ISO, dni with Other, and 4 with ISO certification. To this end the polyethylene coating can be applied without a PE adhesive layer to make sampling easier.

The voltage is to be applied only at the 3067 of measurement. Jet cleaning and any necessary follow-up work should not lead to the reduction of minimum wall thickness specified in the standard of steel pipe technology delivery. However this involves neither an increased risk of corrosion underrusting nor an increase in the protective current density requirement in cathodic corrosion protection.

Catalogue — Ruscomposite JSC

This standard is also available to be included in Standards Subscriptions. Ageing is evaluated by assessing the changes in the polyethylene through the variation in its melt flow rate MFR.

Need more than one copy? DIN EN ISO specifies the international standard requirements for the three tier extruded polyethylene and polypropylene based coatings for oil and gas pipeline transportation systems. Alternative provisions 330670 repairs may be agreed. The sample shall be cut in the cold state.

Heat-shrinkable sleeve “CANUSA GTS-PE 3L”

For three-layer coatings, the epoxy resin and adhesive layers at the pipe ends shall be removed to at least 80 mm from the welding bevel. The minimum layer thickness is 60?

For this reason, a wetting agent test is not specified in this standard. Other test sequences can be agreed.